Liquid Crystal Polymer LCP

HOME > Plastic Products > Liquid Crystal Polymer LCP

Item No : Liquid Crystal polymer LCP
Product Name : Liquid Crystal polymer LCP

Characteristics of LCP
  • l Molecular chains align themselves when molded, and this generates a self-reinforcing effect, Thereby resulting in extremely high strength and elastic modulus.
  • Despite having a high elastic modulus, very much superior vibration absorbing characteristics are exhibited.
  • Linear expansion coefficient in the flow direction in particular is very small, exhibiting a value an order of magnitude less than conventional plastics and on a par with steel.
  • The thinner the product, the higher the proportion of the oriented surface layer, so greater strength and elastic modulus can ge achieved the thinner the product.
  • Because of its microcrystalline structure, LCP possesses superior deflection temperature under load(180-26 0°), continuous usage temperature(200-24 00°C), and solder heat resistance(2600°C for over 10 s, 310 0°C for 10 s), despite its relatively low melting point.
Applications in LCP

Connectors, sockets, LED case, Transistor package, LED(MID), Light sensor, CD pick up parts,Pump parts, Dot printer vase, Shutter plate of camera, headphone parts, inhibitor switch parts,Optical fibre connector...... .

Typical data of LCP

Test items
Test Standard Units GF30-V0 GF40-V0
Glass Fibre - % 30 40
Specific Gravity ASTMD792 - 1.61 1.70
Water Absorption ASTMD570 % <0.1 <0.1
Tensile Strength ASTMD638 Mpa 164 140
Elongation ASTMD638 % 3.0 1.8
Flexural Strength ASTMD790 Mpa 163 198
Flexural Modulus ASTMD790 Mpa 9237 8674
IZOD Notched Impact strength ASTMD256 J/M² 106 85
Rockwell Hardness ASTMD785 R R77 R79
Heat Deflection Temp ASTMD648 °C 280 290
Flammability Rating SGS UL-94 VO(0.8mm) VO(0.8mm)
Moulding Shrinkage TD - % 0.01
All tests were run under laboratory conditions ASTM testing Procedures,The data are intended as general guide only.